| Microstructure Evolution of T6 Treated Electron-beam Welded Al-Zn-Mg-Cu Alloy |
| |
| View Full Text Download reader |
| DOI：10.3969/j.issn.1004-4957.年份.月份 |
| KeyWord:Electron-beam welding Al-Zn-Mg-Cu alloy texture |
| Author | Institution |
| 左玉婷，孙泽明，王峰，熊柏青，张永安，朱宝宏 |
1.北京有色金属研究总院国家有色金属及电子材料分析测试中心;2.北京有色金属研究总院国家有色金属制备与加工重点实验室 |
|
| Hits: 2344 |
| Download times: 925 |
| Abstract: |
| The microstructure and texture evolution of electron-beam welded Al-Zn-Mg-Cu alloy were investigated using field emission scanning electron microscopy，transmission electron microscopy and electron back-scatter diffraction（EBSD）.The results indicated that the weld nugget zone was composed of equiaxed grains with an average grain size of 3-8 μm.The second phases are mainly distributed along the grain boundaries.After T6(solution treated and aged） treatment，Most of the second phases in weld nugget were dissolved into α（Al）.The base metal exhibits the typical<111> and<001> fibre textures in extrusion direction，and the sharpness slightly decreased after T6 treatment.No significant texture was observed in the nugget zone. |
| Close |